Hastelloy合金是镍基合金。它主要是两组;一个有更多钼和另一铬的铬。两者都被称为hastelloy。它们都特别抵抗强氧化溶液,并在还原剂中具有高耐久性。由于低碳含量和焊接较低的碳化物沉淀,它们也抵抗骨间腐蚀。Hastelloy应用程序列表更长。有不同标准制造的不同形式和形状的产品,可用于各种应用。yabo登录app它们用于酸气井,废物处理厂,化学加工组件,纸浆和造纸工业,化工厂,热交换器,风扇和食品加工设备中的反应血管。Hastelloy性质是独特的,因为它们非常耐氧化和减少; they perform well under cryogenic temperatures and in high temperatures, resistant to wet chlorine gas, resistant to most chloride and chlorine derivatives and so on. The Hastelloy price per kg differs from product to product and you can get a full price list from us. There are many Hastelloy advantages over ordinary metal and other alloys. The resistance to localized corrosion is very high along with resistance to uniform corrosion. The resistance is also good against most salts and brackish waters. The Hastelloy abbreviation is used in the metal industry mostly instead using the full form nickel chromium molybdenum alloys. TheHastelloy合金成分包括钼、铬、铁、钨、螺杆、锰、铜、钒、磷、硅和硫。根据合金的等级和标准,其成分也不同。每一类和等级都有特定的特点和应用。哈斯特洛伊供应商销售所有不同等级和不同的产品。yabo登录app产品范围yabo登录app从紧固件到管道和螺栓到轮廓环。其他则哈氏合金,在高温合金家族下许多等级包括等铬镍铁合金&蒙乃尔。
价格 | 56美元/公斤 |
合金 | 爹妈 | 酒吧 | 管道 |
---|---|---|---|
c - 4 |
N06455 |
ASTM B574/ B575/ B619 |
B622 / B619 / SB 619 / B626 / SB 626 |
C-22 |
N06022 |
ASTM B564/ B472/ B574 |
B622 / B619 / SB 619/ B626 / SB 626 |
c - 2000 |
N06200 |
ASTM B564/ B472/ B574 |
B622 / B619 / SB 619/ B626 / SB 626 |
G-30 |
N06030 |
ASTM B472 / B581 |
B622 / B619 / SB 619/ B626 / SB 626 |
G-35 |
N06035 |
ASTM B564/ B472/ B574 |
B622 / B619/ SB 619/ B626 / SB 626 |
C-276. |
N10276 |
ASTM B564/ B472/ B574 |
B622 / B619 / SB 619/ B626 / SB 626 |
Hastelloy X | N06002 | ASTM B564/ B472/ B574 | B622 / B619 / SB 619 B626 / SB 626 |
HAYNES®HR-120, NAS H38X | N08120 | B407 / B514 / B515 |
这些名字 | 美国 | 材料Nr。 |
---|---|---|
合金的名字 | 爹妈 | WNR |
b - 2 | N10665 | DIN 2.4617 |
C | n10002 | |
c - 4 | N06455 | DIN 2.4610 |
C-276. | N10276 | DIN 2.4819 |
G | N06007 | |
三大 | N06985 | DIN 2.4619 |
N | n10003. | |
年代 | N06635 | |
W | N10004. | |
X | N06002 | DIN 2.4665 |
HASTELLOY®酮®合金 | 400 - 450℃(750 - 840华氏度) |
C-22 | 400 - 450℃(750 - 840华氏度) |
C-276. | 870 - 1230℃(1600 - 2250华氏度) |
®N合金 | 704至871℃(1300至1600华氏度) |
海恩斯®25合金 | 980℃(1800华氏度) |
Haynes®188合金 | 1095DEG C(2000度F) |
合金类型 | Cr % | C % | 有限公司% | W % | 密苏里州% | V % | Ai % | Ti % | Nb % | 菲% | CU% | 倪% | 其他% |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
合金B | 0.6 | 0.1 | 1.25 | - | 28 | 0.3 | - | - | - | 5.5 | - | rest /落下帷幕 | MN 0.80;如果0.70 |
合金B2 | 1 | 0.02 | 1 | - | 26.0-30.0. | - | - | - | - | 2 | - | rest /落下帷幕 | Mn 1.0, Si 0.10 |
合金C276 | 14.0 - -16.5 | 0.02 | 2.5 | 3.0 - -4.5 | 15.0 - -17.0 | 0.35 | - | - | - | 4.0 - -7.0 | - | rest /落下帷幕 | Mn 1.0;如果0.05 |
合金X | 22 | 0.1 | 1.5 | 0.6 | 9 | - | - | 18.5 | - | - | - | rest /落下帷幕 | Mn 0.6;如果0.60 |
合金C | 16 | 0.07 | 1.25 | 40 | 17 | 0.3 | - | - | - | 5.75 | - | rest /落下帷幕 | Mn 1.0;如果0.70 |
合金C4 | 14.0 - -18.0 | 0.015 | 2 | - | 14.0 - -17.0 | - | - | 70年0 . . | - | 3. | - | rest /落下帷幕 | Mn 1.0;如果0.08 |
合金N | 7 | 0.06 | 0.25 | 0.2 | 16.5 | - | - | - | - | 3. | 0.1 | rest /落下帷幕 | Mn 0.40;如果0.25;B 0.01 |
合金年代 | 15.5 | 0.02 | 2 | 1 | 14.5 | 0.6 | 0.2 | - | - | 3. | - | rest /落下帷幕 | Mn 0.50;如果0.40;B0.0009;洛杉矶0.02 |
合金F | 22 | 0.02 | 1.25 | 0.5 | 6.5 | - | - | - | 2.1 | 21 | - | rest /落下帷幕 | Mn 1.50;如果0.50 |
合金G | 21.0 - -23.5 | 0.05 | 2.5 | 1 | 5.5 - -7.5 | - | - | - | 1.7 - -2.5 | 18.0 - -21.0 | 1.5 - -2.5 | rest /落下帷幕 | Mn 1.0-2.0;P0.04;SI 1.0; |
合金G2 | 23.0-26.0. | 0.03 | - | - | 5.0 - -7.0 | - | - | 0.70 - -1.50 | - | rest /落下帷幕 | 0.70 - -1.20 | 47.0 - -52.0 | Mn 1.0;如果1.0 |
合金W | 5 | 0.06 | 1.25 | - | 24.5 | - | - | - | - | 5.5 | - | rest /落下帷幕 | Mn 0.050;如果0.50 |
合金的名字 | 临界点蚀温度 在酸性6% FeCl3中 |
酸化6% FeCl3临界缝隙温度 |
||
---|---|---|---|---|
°F | °C | °F | °C | |
316升 | 59 | 15 | 32 | 0 |
254 smo | 140 | 60 | 86 | 30. |
625 | 212. | 100. | 104. | 40 |
C-276. | > 302 | > 150 | 131 | 55 |
C-22® | > 302 | > 150 | 176 | 80 |
年级 | 开裂时间 |
---|---|
316升 | 2小时 |
254 smo | 24小时 |
625 | 1008小时不开裂 |
C-276. | 1008小时不开裂 |
C-22® | 1008小时不开裂 |
年级 | 静 | 流动 | ||
---|---|---|---|---|
攻击网站数量 | Max。深度 | 攻击网站数量 | Max。深度 | |
316升 | 答:2,B: 2 | 答:1.33,2.27 | 答:2,B: 2 | 答:0.48,0.15 |
254 smo | 答:2,B: 2 | 答:0.76,1.73 | 答:2,B: 2 | 答:0.01,B: < 0.01 |
625 | 答:1,B: 2 | 答:0.18,0.04 | 答:2,B: 2 | 答:< 0.01,< 0.01 |
C-276. | 答:1,B: 1 | 答:0.10,0.13 | 答:0,B: 0 | 答:0,B: 0 |
C-22® | 答:0,B: 0 | 答:0,B: 0 | 答:0,B: 0 | 答:0,B: 0 |
HRB =洛氏硬度“B”。
Hastelloy年级 | 床单HRB. | 盘子HRB |
---|---|---|
C22. | 93 | 95 |
C276 | 90 | 87 |
N | 96 | - |
X | 54 | 54 |
有关详细信息,请参阅https://haynesintl.com/alloys/alloy-portfolio_#High-temperature-Alloys